A composition of a porous body for use as biomaterial according to the
present invention is produced by adding Al (aluminum) in the amount of 0.1
to 3.0 atomic % to a porous composition consisting of titanium, nickel,
iron and molybdenum, and it promotes the growth of living tissue and cells
into pores. By the addition of Al to Ni, Ti, Fe and Mo, the temperature of
formation of the liquid phase is lowered, and thus the diffusion of the
constitutional elements of the composition is promoted, and the uniform
distribution of the constitutional elements increases. As a result, the
proportion of micropores in the porous body becomes increased to the
extent that the distribution of micropores having the size in the range of
10.sup.-2 .mu.m.about.10 .mu.m is more than 5% in the metal bridge.
Uma composição de um corpo poroso para o uso como o biomaterial de acordo com a invenção atual é produzida adicionando o al (alumínio) na quantidade de 0.1 a 3.0 % atômico a um titânio consistindo, niquelar, a um ferro e a um molibdênio da composição porosa, e promove o crescimento de tecido e de pilhas vivos em pores. Pela adição do al ao Ni, ao ti, ao Fe e ao Mo, a temperatura da formação da fase líquida é abaixada, e a difusão dos elementos constitutional da composição é promovida assim, e a distribuição uniforme dos aumentos constitutional dos elementos. Em conseqüência, a proporção dos micropores no corpo poroso torna-se aumentada até ao ponto em que a distribuição dos micropores que têm o tamanho na escala do mu.m do mu.m.about.10 10.sup.-2 é mais de 5% na ponte do metal.