The invention is to offer such a dielectric ceramic enabling to
simultaneously sinter with the low resistant conductor of Ag based metals
and Cu based metals, having the excellent mechanical strength and
exhibiting the excellent dielectric characteristics in the GHz zone. Mixed
powders of Si: 20 to 30 weight %, B: 5 to 30 weight %, Al: 20 to 30 weight
%, Ca: 10 to 20 weight %, and Zn: 10 to 20 weight % are prepared, melted,
and rapidly cooled to produce glass frits. The glass frits are granulated
and mixed with gahnite filler and titania filler which are inorganic
filler powders. Subsequently, a binder is thrown into the powders to
produce a composition of dielectric ceramic, and then is formed, followed
by sintering. The mixed powders may contain at least one kind of alkali
metal of Li, K and Na.
La invención es ofrecer permitir de cerámica tan dieléctrico sinterizar simultáneamente con el conductor resistente bajo de los metales bajos del AG y de los metales bajos del Cu, tener la fuerza mecánica excelente y la exhibición de las características dieléctricas excelentes en la zona del gigahertz. Polvos mezclados del silicio: 20 a 30 pesos %, B: 5 a 30 pesos %, al: 20 a 30 pesos %, CA: 10 a 20 pesos %, y zn: 10 a 20 pesos % están preparados, derretidos, y refrescados rápidamente para producir las fritas de cristal. Las fritas de cristal se granulan y se mezclan con el llenador del gahnite y el llenador del titania que son polvos inorgánicos del llenador. Posteriormente, una carpeta se lanza en los polvos para producir una composición de de cerámica dieléctrico, y después es formada, seguido sinterizando. Los polvos mezclados pueden contener por lo menos una clase de metal alcalino del li, de K y del Na.