The present invention is directed to compositions and a process leading to
colorless or light colored aqueous phicinol-formaldelhyde resoles. Unlike
previous technologies, these compositions lead to clear storage stable
fast curing, high molecular weight resins. These materials are also
capable of producing composite wood panels with superior water absorption
and thickness swell test results when soaked in water. The invention
essentially consists of an aqueous copolymer of phenol, formaldehyde, and
a phenolic carboxylate (e.g. salicylic acid). Methylol phenols are formed
under alkaline conditions in the presence of metal chelating agents. These
are then condensed into a polymer under alkaline, neutral or acidic
conditions. The finished aqueous polymer solution is then acidified to the
desired pH using a benzoic acid or a phelnol-carboxylic acid.
Die anwesende Erfindung wird auf Aufbau und einen Prozeß, der zu farblosen oder hellen farbigen wäßrigen phicinol-formaldelhyde neu besohlen führt verwiesen. Anders als vorhergehende Technologien führt dieser Aufbau zu freies Speicherdas beständige schnelle Kurieren, Molekulargewichtharze. Diese Materialien sind auch zum Produzieren der zusammengesetzten hölzernen Verkleidungen mit überlegenen Wasserabsorption und Stärke Schwellentestergebnissen fähig, wenn sie im Wasser getränkt werden. Die Erfindung besteht im Wesentlichen aus einem wäßrigen Copolymer des Phenols, des Formaldehyds und des phenoplastischen Karboxylats (z.B. Salizyl- Säure). Methylol Phenole werden unter alkalischen Bedingungen in Anwesenheit der Metallcheliermittel gebildet. Diese werden dann in ein Polymer-Plastik unter den alkalischen, Null- oder säurehaltigen Bedingungen kondensiert. Die fertige wäßrige Polymer-Plastik Lösung wird dann zum gewünschten pH mit einer Benzoesäure oder einer phelnol-karboxylhaltigen Säure gesäuert.