A TiAl based alloy having excellent strength as well as an improvement in toughness at room temperature, in particular an improvement in impact properties at room temperature, and a production method thereof, and a blade using the same are provided. This TiAl based alloy has a microstructure in which lamellar grains having a mean grain diameter of from 1 to 50 .mu.m are closely arranged. The alloy composition is Ti-(42-48)Al-(5-10) (Cr and/or V) or Ti-(38-43)Al-(4-10)Mn. The alloy can be obtained by subjecting the alloy to high-speed plastic working in the cooling process, after the alloy has been held in an equilibrium temperature range of the .alpha. phase or the (.alpha.+.beta.) phase.

Обеспечен сплав основанный TiAl имея превосходную прочность также,как улучшение в toughness на температуре комнаты, в частности улучшение в свойствах удара на температуре комнаты, и способа производства thereof, и лезвие используя эти же. Этот сплав основанный TiAl имеет микроструктуру в тонкослоистые зерна имея средний диаметр зерна от mu.m 1 до 50 близко аранжированы. Составом сплава будет ti-(42-48)Al-(5-10)-(42-48)Al-(5-$$ET-10) (cr and/or в) или Ti-(38-43)Al-(4-10)Mn. Сплав может быть получен путем подвергать сплав к высокой пластмассе скорости работая в охлаждая процессе, после того как сплав держался в температурной амплитуде уравновешения участка alpha. или (alpha.+.beta.) участок.