A dental resin material mixed with a composition containing, as a
maincomponent, titanium dioxide whose surface has been partly coated with
apatite. In the dental resin material, it is preferable that anatase-,
rutile-, brookit-type titanium dioxide or a mixture of these components is
used as the titanium dioxide. The apatite for partial coating of titanium
dioxide is produced by immersing powdery titanium dioxide in a pseudo body
fluid and stirring the immersed titanium dioxide approximately at the same
temperature as a human body temperature, i.e., 36.degree. C. In this
instance, it is important that the apatite is deposited in the form of
platy crystals of less than 2 mm in thickness to cover 0.001-10% of the
surface of titanium dioxide.
Ένα οδοντικό υλικό ρητίνης που αναμιγνύεται με μια σύνθεση που περιέχει, ως maincomponent, διοξείδιο τιτανίου η του οποίου επιφάνεια έχει ντυθεί εν μέρει με apatite. Στο οδοντικό υλικό ρητίνης, είναι προτιμητέο ότι το anatase -, rutile -, το διοξείδιο τιτανίου ψροοκητ-τύπων ή ένα μίγμα αυτών των συστατικών χρησιμοποιούνται ως διοξείδιο τιτανίου. Apatite για το μερικό επίστρωμα του διοξειδίου τιτανίου θερμοκρασία παράγεται με τη βύθιση του κωνιώδους διοξειδίου τιτανίου σε ένα ψευδο ρευστό σωμάτων και το ανακάτωμα του βυθισμένου διοξειδίου τιτανίου περίπου στην ίδια θερμοκρασία με μια ανθρώπινων σωμάτων, δηλ., 36.degree. γ. Σε αυτήν την περίπτωση, είναι σημαντικό ότι apatite κατατίθεται υπό μορφή platy κρυστάλλων λιγότερο από 2 χιλ. στο πάχος για να καλύψει 0,001-10% της επιφάνειας του διοξειδίου τιτανίου.