A heat treated steel strap usable in a strapping machine has a tensile
strength of at least about 170 KSI, and an elongation of at least about
6.5 percent. The steel strap is fabricated from a coiled steel reduced by
cold rolling. The strap has a composition of 0.30 to 0.36 percent carbon,
0.90 to 1.25 percent manganese, and 0.75 to 1.10 percent silicon. The
strap is heated to a temperature of about 815.degree. C. to about
900.degree. C. and quenched to a temperature of about 370.degree. C. to
about 510.degree. C. The strap has a seal joint break strength of about
4350 pounds when the strap has a width of about one inch and a thickness
of 0.030 inches. A method for forming the strap is also disclosed.
Планка обработанная жарой стальная годная к употреблению в связывая машине имеет прочности на растяжку по крайней мере около 170 KSI, и удлиненность по крайней мере около 6.5 процентов. Стальная планка изготовлена от спиральной стали уменьшенной холодной завальцовкой. Планка имеет состав от 0.30 до 0.36 процентов углерода, от 0.90 до 1.25 процентов марганца, и от 0.75 до 1.10 процентов кремния. Планка нагрета к температуре около 815.degree. C к около 900.degree. C и погашено к температуре около 370.degree. C к около 510.degree. Ч. Планка имеет прочность пролома соединения уплотнения около 4350 фунтов когда планка имеет ширину около одного дюйма и толщину 0 030 дюймов. Метод для формировать планку также показан.