Methods of manufacturing hot-dip galvanized hot-rolled and cold-rolled steel sheets excellent in strain age hardening property

   
   

The present invention provides a steel sheet having a chemical composition comprising 0.15% or less C, 2.0% or less Si, 3.0% or less Mn, P, S, Al and N in adjusted amounts, from 0.5 to 3.0% Cu, or one or more of Cr, Mo and W in a total amount of 2.0% or less, and having a composite structure comprising ferrite and martensite having an area ratio of 2% or more. The steel sheet is in the form of a high-strength hot-rolled steel sheet, a high-strength cold-rolled steel sheet, or a hot-dip galvanized steel sheet. There is thus available a steel sheet excellent in press-formability and in strain age hardening property as represented by a .DELTA.TS of 80 MPa or more.

A invenção atual fornece uma folha de aço que tem uma composição química compreender 0.15% ou menos 2.0% ou menos do silicone, 3.0% ou a menos manganês de C, P, S, al e N em quantidades ajustadas, o cu 0.5 a 3.0%, ou o um ou o mais do cr, do Mo e do W em uma quantidade total de 2.0% ou mais menos, e ter uma estrutura composta compreender o ferrite e o martensite que têm uma relação da área de 2% ou mais. A folha de aço está no formulário de uma folha de aço hot-rolled high-strength, uma folha de aço cold-rolled high-strength, ou quente-mergulhe a folha de aço galvanized. Há assim disponível uma folha de aço excelente em pressiona-formability e na idade da tensão que endurece a propriedade como representado pelo DELTA.TS De 80 MPa ou mais.

 
Web www.patentalert.com

< Tire with specified rubber-steel cord composite

< Steel strap composition

> Method for determining alloy phase in plating layer and method for evaluating sliding property of alloy galvanized steel plate

> Mortar composition of at least two components and curable by heat initiation and a method for fastening tie rods, reinforcing steel for concrete or the like in solid substrates

~ 00143