The present invention provides a polymer blend suitable for use as a film
or a coating, the polymer blend including from 1 to 99% by weight of a
metallocene-produced VLDPE polymer having a density less than 0.916
g/cm.sup.3, and from 1 to 99% by weight of an LDPE polymer having a
density of from 0.916 to 0.928 g/cm.sup.3 wherein the sum of (a) and (b)
is 100%. The VLDPE polymer can have a melt index of from 6 to 15 dg/min,
or from 9 to 12 dg/min. The present invention further provides polymeric
films extrusion cast from such polymer blends, and articles having a
flexible substrate and a polymeric film extrusion-coated on the substrate
La presente invenzione fornisce una miscela del polimero adatta per uso come una pellicola o rivestimento, la miscela del polimero che include 1 - 99% del peso di un polimero metallocene-prodotto di VLDPE che ha una densità più meno di 0.916 g/cm.sup.3 e 1 - 99% del peso di un polimero del LDPE che ha una densità di 0.916 - 0.928 g/cm.sup.3 in cui la somma di (a) e di (b) è 100%. Il polimero di VLDPE può avere un indice della fusione di 6 - 15 dg/min, o 9 - 12 dg/min. La presente invenzione ulteriore fornisce il getto polimerico dell'espulsione delle pellicole da tali miscele del polimero ed articoli che hanno un substrato flessibile e una pellicola polimerica espulsione-rivestiti sul substrato