A method of preparing a mortar composition, comprising mixing of mortar
materials comprising at least 25 to 45 parts by weight of
high-early-strength portland cement, 40 to 60 parts by weight of sand,
0.05 to 0.12 parts by weight of polycarboxylic acid-based powdered water
reducing agent, and 10 to 25 parts by weight of water, and not comprising
any organic adhesives. Mixing of the mortar materials is achieved by
agitating the same in an agitator until agitating load rapidly decreases.
The mortar composition prepared in accordance with this invention has
excellent ability to infiltrate into the surface to be adhered, and high
bonding strength after hardening.
Um método de preparar uma composição do almofariz, compreendendo misturar dos materiais do almofariz que compreendem ao menos 25 a 45 porções pelo peso do cimento de portland da elevado-cedo-força, 40 a 60 porções pelo peso da areia, 0.05 a 0.12 porção pelo peso do agente reduzindo-se pulverizado acid-based polycarboxylic da água, e 10 a 25 porções pelo peso da água, e não compreendendo alguns adesivos orgânicos. Misturar dos materiais do almofariz está conseguido agitando o mesmo em um agitador até que a carga agitando diminua ràpidamente. A composição do almofariz preparou-se de acordo com esta invenção tem a abilidade excelente de infiltrate na superfície a ser aderida, e a força elevada da ligação após endurecer-se.