A method for manufacturing foam pads includes a first step of preparing a proper amount of PVC power, DOP curing agent, light calcium carbonate, kaolin, foaming agent and pigment and pouring them into a blending device to be blended and form a liquid starchy material. Next, the liquid starchy material is conveyed into an intermediate material barrel and kept stationary for pre-foaming at normal temperature for about 8 hours and then coated on a conveyer pelt to form a starchy material layer. Subsequently, the starchy material layer is kept stationary and heated at 80-90.degree. C. for about 3-10 minutes and then continuously heated at 185-200.degree. C. for about 20-30 minutes to form an integral-sheeted foam pad. After cooled, the integral-sheeted foam pad is thermo-compressed and cut into various foam pad products.

 