A mixture of carbon-containing fibers, such as mesophase or isotropic pitch
fibers, a suitable matrix material, such as a milled pitch is compressed
while resistively heating the mixture to form a carbonized composite
material. Preferably, the carbonized material has a density of at least
about 1.30 g/cm.sup.3. Preferably, the composite material is formed in
less than ten minutes. This is a significantly shorter time than for
conventional processes, which typically take several days and achieve a
lower density material. A treating component may be impregnated into the
composite. Consequently, carbon composite materials having final densities
of about 1.6-1.8 g/cm.sup.3 or higher are readily achieved with one or two
infiltration cycles using a pitch or other carbonaceous material to fill
voids in the composite and rebaking.
Ένα μίγμα άνθρακας-περιορισμού των ινών, τέτοιων ως μεσόφαση ή των ισοτροπικών ινών πισσών, ένα κατάλληλο υλικό μητρών, τέτοια ως αλεσμένη πίσσα συμπιέζεται resistively θερμαίνοντας το μίγμα για να διαμορφώσει ένα ανθρακωμένο σύνθετο υλικό. Κατά προτίμηση, το ανθρακωμένο υλικό έχει μια πυκνότητα τουλάχιστον περίπου 1,30 γ/cm.sup.3. Κατά προτίμηση, το σύνθετο υλικό διαμορφώνεται σε λιγότερο από δέκα λεπτά. Αυτό είναι ένας σημαντικά πιό σύντομος χρόνος απ'ό,τι για τις συμβατικές διαδικασίες, οι οποίες παίρνουν χαρακτηριστικά αρκετές ημέρες και επιτυγχάνουν ένα υλικό χαμηλότερης πυκνότητας. Ένα τμήμα μεταχείρησης μπορεί να γονιμοποιηθεί στο σύνθετο. Συνεπώς, τα σύνθετα υλικά άνθρακα που έχουν τις τελικές πυκνότητες περίπου 1.6-1.8 γ/cm.sup.3 ή υψηλότερος επιτυγχάνονται εύκολα με έναν ή δύο κύκλους διήθησης χρησιμοποιώντας μια πίσσα ή άλλο ανθρακούχο υλικό για να γεμίσουν τα κενά στο σύνθετο και.