A method of producing electrodes for electrolytic capacitors by etching
metal foil in a low pH etching electrolyte is disclosed. The low pH
electrolyte is an aqueous solution, which comprises hydrochloric acid,
glycerol, sodium perchlorate or perchloric acid, sodium persulfate and
titanium (111) chloride. Anode foils etched according to the method of the
invention maintain high capacitance gains, electrical porosity and
strength. The electrical porosity of the etched foils is sufficiently high
such that the overall Equivalent Series Resistance (ESR) is not increased
in multilayer anodes configurations. Also described is a low pH
electrolyte bath composition. Anode foils etched according to the present
invention and electrolytic capacitors incorporating the etched anode foils
are also disclosed.
Un metodo di produrre gli elettrodi per i condensatori elettrolitici incidendo il metallo all'acquaforte sventa in un elettrolito basso acquaforte di pH è rilevato. L'elettrolito basso di pH è una soluzione acquosa, che contiene l'acido cloridrico, glicerolo, perclorato del sodio o acido, persolfato del sodio e cloruro perclorici del titanio (111). L'anodo sventa inciso secondo il metodo dell'invenzione effettua gli alti guadagni di capacità, la porosità elettrica e la resistenza. La porosità elettrica del inciso sventa è sufficiente alta tali che la resistenza equivalente generale di serie (esr) non è aumentata di configurazioni a più strati degli anodi. Inoltre è descritta una composizione del bagno bassa dell'elettrolito di pH. L'anodo sventa inciso secondo la presente invenzione ed i condensatori elettrolitici che incorporano l'anodo inciso sventa inoltre sono rilevati.