The present invention contemplates water-bearing silicate materials
achieved by modifying the basic method of essentially reacting water glass
with calcium chloride to bind the free water into solid form without
adversely affecting the basic chemical and physical structure of the
original product. The material is then dried by using a physical wicking
agent, such as a cellulose sponge, adding an anhydrous salt to the
material to form a crystalline hydrate, or adding calcium oxide or calcium
hydroxide to the material to form a microstructure that physically retains
the water. The material is then incorporated into a fire protection
container in which the material forms the outermost wall of the container,
a light-weight porous material such as urethane foam an intermediate
layer, and a phase change material with a melting point of around 70
degrees F. to 125 degrees F. forms the innermost wall.
La actual invención comtempla los materiales acuíferos del silicato alcanzados modificando el método básico esencialmente de reaccionar el cristal del agua con el cloruro de calcio para atar el agua libre en forma sólida sin al contrario afectar el producto químico básico y la estructura física del producto original. El material entonces es secado usando un agente wicking físico, tal como una esponja de celulosa, agregando una sal anhidra al material para formar un hidrato cristalino, o agregando el óxido de calcio o el hidróxido de calcio al material para formar una microestructura que conserve físicamente el agua. El material entonces se incorpora en un envase de la protección contra los incendios en el cual el material forme la pared exterior del envase, un material poroso ligero tal como espuma del urethane a la capa intermedia, y un material del cambio de la fase con un punto de fusión de alrededor 70 grados de F. a 125 grados de F. forma la pared íntima.