A nanowire comprising only metal having an average length of 1 .mu.m or
more which could not be produced in the prior art, and a method of
manufacturing this wire.
This invention provides a method of manufacturing a metal nanowire, which
comprises the step of reducing a nanofiber comprising a metal complex
peptide lipid formed from the two-headed peptide lipid represented by the
general formula (I):
##STR1##
in which Val is a valine residue, m is 1-3 and n is 6-18, and a metal ion,
using 5-10 equivalents of a reducing agent relative to the two-headed
peptide lipid. It further provides a metal nanowire having an average
diameter of 10-20 nm and average length of 1 .mu.m or more. It is
preferred that the metal is copper.
Nanowire состоя из только металла имея среднюю длину 1 mu.m или больше не смогла быть произведена в прежнем искусствое, и метод изготовлять этот провод. Этот вымысел обеспечивает метод изготовлять nanowire металла, которое состоит из шага уменьшения nanofiber состоя из липида пептида металла сложного сформированного от двухголового липида пептида представленного вообще формулой (i): ## ## STR1 в которое Val будет выпаркой валина, м 1-3 и н будет 6-18, и ионом металла, использующ 5-10 эквивалентов разбавителя по отношению к двухголовому липиду пептида. Он более добавочно обеспечивает nanowire металла имея средний диаметр 10-20 nm и средняя длина 1 mu.m или больше. Предпочесно что металл будет медью.