A ferritic non-ridging stainless steel and process therefor. A chromium
alloyed steel melt containing sufficient titanium and nitrogen but a
controlled amount of aluminum is cast into an ingot or continuously cast
into a strip or a slab having an as-cast fine equiaxed grain structure
substantially free of columnar grains. The as-cast steel contains 0.08% C,
at least about 8% Cr, up to 1.50% Mn, <0.020% Al, .ltoreq.0.05% N,
.ltoreq.1.5% Si, <2.0% Ni, Ti.gtoreq.0.10%, the ratio of
(Ti.times.N)/Al.gtoreq.0.14, all percentages by weight, the balance Fe and
residual elements. Preferably, the titanium is controlled so that
(Ti/48)/[(C/12)+(N/14)]>1.5. A hot processed sheet may be formed from a
continuously cast slab without grinding the surfaces of the slab. The hot
processed sheet may be descaled, cold reduced to a final thickness and
recrystallization annealed. Annealing the hot processed sheet prior to
cold reduction is not required to obtain an annealed sheet essentially
free of ridging and having high formability.
Um aço inoxidável e um processo non-ridging ferritic therefor. Um cromo alloyed o derretimento de aço que contem o titânio e o nitrogênio suficientes mas uma quantidade de alumínio controlada é moldada em um ingot ou continuamente o molde em uma tira ou em uma laje que têm como-moldou equiaxed muito bem a estrutura da grão substancialmente livre de grões columnar. Como-molde o aço contem 0.08% C, ao menos cr de aproximadamente 8%, até 1.50% manganês, 1.5. Uma folha processada quente pode ser dada forma continuamente de uma laje do molde sem moer as superfícies da laje. A folha processada quente pode descaled, frio ser reduzida a uma espessura final e recrystallization recozido. Recozer a folha processada quente antes da redução fria não é requerido para obter essencialmente uma folha recozida livre de ridging e de ter o formability elevado.