By rapidly heating a precursor wire having a multifilamentary structure in
which multiple composite cores in which a composite compound of an Nb--Ga
compound and Nb is embedded in Nb are embedded in Nb, Ta, Nb-base alloy or
Ta-base alloy as a matrix material to a temperature range of 1400 to
2100.degree. C. in 2 seconds, quenching the precursor wire at a rate of
5000.degree. C./second or larger, and subjecting the precursor wire to
additional heat treatment at a temperature range of 600 to 850.degree. C.
for 1 to 400 hours, a superconducting wire having a multifilamentary
structure in which multiple composite cores in which a composite compound
containing Nb.sub.3 Ga of a stoichiometric composition embedded in Nb are
embedded in Nb, Ta, Nb-base alloy or Ta-base alloy as a matrix material is
obtained.
быстро нагревать прекурсор свяжите проволокой иметь multifilamentary структуру в множественные составные сердечники в составная смесь N B -- смесь Ga и N B врезаны в N B врезаны в N B, ta, сплаве N B-$$ET-osnovani4 или сплаве Та-osnovani4 как материал матрицы к температурной амплитуде 1400 к 2100.degree. C в 2 секундах, гася провод прекурсора на тарифе 5000.degree. C./second или большой, и подвергать провод прекурсора к дополнительной обработке жары на температурной амплитуде 600 к 850.degree. Ч. на от 1 до 400 часов, superconducting провод имея multifilamentary структуру в которой множественные составные сердечники в которых составное составное содержа Nb.sub.3 Ga стехиометрического состава врезанного в N B врезано в N B, ta, сплаве N B-$$ET-osnovani4 или сплаве Та-osnovani4 по мере того как материал матрицы получен.