Compositions are provided for increasing the electrical conductivity of
concrete or controlled low-strength materials (flowable fill). One
composition sets to produce a concrete and includes from 1% to 30% by
weight of portland cement; from 1% to 30% by weight of fly ash having a
carbon content as measured by loss on ignition of greater than 12%; from
40% to 90% by weight of an aggregate; from 0.1% to 20% by weight of carbon
fibers; and water in a sufficient amount such that the composition sets to
a concrete. Another composition is a self-compacting, cementitious
flowable fill composition that includes from 1% to 30% by weight of
portland cement; from 5% to 85% by weight of fly ash; from 0.1% to 20% by
weight of carbon fibers; and water in a sufficient amount such that the
composition sets to a material having a compressive strength of 8.3 MPa or
less.
De samenstellingen worden verstrekt voor het verhogen van het elektrogeleidingsvermogen van concrete of gecontroleerde low-strength flowable materialen (vul). Één samenstelling plaatst om een beton te produceren en omvat van 1% tot 30% bij het gewicht van portlandcement; van 1% tot 30% bij het gewicht van vliegas die een koolstofinhoud heeft zoals die door verlies op ontsteking van groter wordt gemeten dan 12%; van 40% tot 90% bij het gewicht van een complex; van 0,1% tot 20% bij het gewicht van koolstofvezels; en water in een voldoende bedrag dusdanig dat de samenstellingsreeksen aan een beton. Een andere samenstelling is zelf-samenperst, cementitious vult flowable samenstelling die van 1% tot 30% bij het gewicht van portlandcement omvat; van 5% tot 85% bij het gewicht van vliegas; van 0,1% tot 20% bij het gewicht van koolstofvezels; en water in een voldoende bedrag dusdanig dat de samenstellingsreeksen aan een materiaal dat een samenpersende sterkte van 8,3 MPa of minder heeft.