A steel sheet composition contains appropriate amounts of C, Si, Mn, P, S,
Al and N and 0.5 to 3.0% Cu. A composite structure of the steel sheet has
a ferrite phase or a ferrite phase and a tempered martensite phase as a
primary phase, and a secondary phase containing retained austenite in a
volume ratio of not less than 1%. In place of the Cu, at least one of Mo,
Cr, and W may be contained in a total amount of not more than 2.0%. This
composition is useful in production of a high-ductility hot-rolled steel
sheet, a high-ductility cold-rolled steel sheet and a high-ductility
hot-dip galvanized steel sheet having excellent press formability and
excellent stain age hardenability as represented by a .DELTA.TS of not
less than 80 MPa, in which the tensile strength increases remarkably
through a heat treatment at a relatively low temperature after press
forming.
Состав стального листа содержит соотвествующее количество ч, кремния, марганца, п, с, al и н и cu 0.5 до 3.0%. Составная структура стального листа имеет участок феррита или участок феррита и закаленный участок martensite как первичный участок, и вторичный участок содержа сохраненное austenite в коэффициенте тома более менее чем 1%. In place of cu, по крайней мере один из mo, cr, и ш могут содержаться в полнаяа сумма больше чем 2.0%. Этот состав полезн в продукции листа высок-duktil6nosti горячекатаного стального, листа холоднопрокатного высок-duktil6nost6h стального и высок-duktil6nost6 горяч-okunaet гальванизированный стальной лист имея превосходное formability давления и превосходную закаливаемость времени пятна как представлено DELTA.TS меньш чем 80 MPa, в котором прочности на растяжку увеличивает замечательн через обработку жары на относительно низкой температуре после формировать давления.