Refractory metal layers 2, 4, 6, 8, and 10, and rare earth alloy magnetic
layers 3, 5, 7, 9, 11, and 12 are alternately deposited, so as to form a
multilayer structure including four or more layers on a substrate. The
refractory metal layers 2, 4, 6, 8, and 10 are formed from at least one
kind of material selected from a group consisting of Ti, V, Cr, Zr, Nb,
Mo, Hf, Ta, and W, and each has a thickness of not less than 5 nm nor more
than 50 nm. The rare earth alloy magnetic layers 3, 5, 7, 9, 11, and 12
have tetragonal R.sub.2 Fe.sub.14 B (R is Nd and/or Pr) as a primary
constituent phase, and each has a thickness of not less than 50 nm nor
more than 500 nm.
Il metallo refrattario fa uno strato di 2, 4, 6, 8 e 10 e gli strati magnetici 3, 5, 7, 9, 11 e 12 della lega della terra rara alternatamente sono depositati, in modo da formare una struttura a più strati compreso quattro o più strati su un substrato. Il metallo del refrattario fa uno strato di 2, 4, 6, 8 e 10 sono formati almeno da un genere di materiale scelto da un Ti del gruppo, da un V, da un Cr, da uno Zr, da una N.B.:, da un Mo, da un'HF, dall'AT e da un W consistenti e ciascuno ha uno spessore di 5 nm né più di di 50 nm. Gli strati magnetici 3, 5, 7, 9, 11 e 12 della lega della terra rara hanno R.sub.2 tetragonal Fe.sub.14 B (R è ND e/o fotoricettore) come fase costituente primaria e ciascuno ha uno spessore di 50 nm né più di di 500 nm.