The subject apparatus provides a means to produce UCl.sub.3 in large
quantities without incurring corrosion of the containment vessel or
associated apparatus. Gaseous Cl is injected into a lower layer of Cd
where CdCl.sub.2 is formed. Due to is lower density, the CdCl.sub.2 rises
through the Cd layer into a layer of molten LiCl--KCL salt where a
rotatable basket containing uranium ingots is suspended. The CdCl.sub.2
reacts with the uranium to form UCl.sub.3 and Cd. Due to density
differences, the Cd sinks down to the liquid Cd layer and is reused. The
UCl.sub.3 combines with the molten salt. During production the temperature
is maintained at about 600.degree. C. while after the uranium has been
depleted the salt temperature is lowered, the molten salt is pressure
siphoned from the vessel, and the salt product LiCl--KCl-30 mol %
UCl.sub.3 is solidified.
O instrumento sujeito fornece meios produzir UCl.sub.3 em quantidades grandes sem incorrer a corrosão da embarcação do containment ou do instrumento associado. O cl gasoso é injetado em uma camada mais baixa de Cd onde CdCl.sub.2 é dado forma. devido a é uma densidade mais baixa, as ascensões CdCl.sub.2 com a camada do Cd em uma camada de liCl derretido -- sal de KCL onde uma cesta rotatable que contem os ingots de urânio é suspendida. O CdCl.sub.2 reage com o urânio ao formulário UCl.sub.3 e ao Cd. devido às diferenças da densidade, o Cd afunda-se para baixo à camada líquida do Cd e reúso. As ligas UCl.sub.3 com o sal derretido. Durante a produção a temperatura é mantida aproximadamente em 600.degree. C. quando depois que o urânio estêve esgotado a temperatura de sal for abaixada, o sal derretido é pressão extraído com sifão da embarcação, e o liCl do produto de sal -- o mol de % de KCl-30 UCl.sub.3 solidified.