The invention relates to polymer ceramic composite materials with a
virtually zero shrinkage compared to the original model after concluding
partial pyrolysis and with a comparable thermal expansion behavior
(preferably in an application range of 400.degree. C. or less) to metal
construction materials, in particular gray cast iron or steel, which are
obtainable by methods described below; corresponding composite
constructions and molded parts; and methods for producing and using these
materials, composite constructions and molded parts. The polymer ceramic
composite materials can for instance be used instead of or in contact with
steel or gray cast iron temperature-proof molded parts, predominantly in
mechanical engineering, without postmachining after the creative forming.
De uitvinding heeft op polymeer ceramische samengestelde materialen betrekking met een vrijwel nul inkrimping in vergelijking met het originele model na het besluiten van gedeeltelijke pyrolyse en met een vergelijkbaar thermische uitbreidingsgedrag (bij voorkeur in een toepassingswaaier van 400.degree. C. of minder) aan metaalbouwmaterialen, in het bijzonder grijs gietijzer of staal, die door hieronder beschreven methodes verkrijgbaar zijn; overeenkomstige samengestelde bouw en gevormde delen; en methodes om deze materialen, samengestelde bouw en gevormde delen te veroorzaken en te gebruiken. De polymeer ceramische samengestelde materialen kunnen bijvoorbeeld in plaats van of in contact met staal of grijze gietijzer temperatuur-bewijs gevormde delen, hoofdzakelijk in werktuigbouw worden gebruikt, zonder het postmachining na zich het creatieve vormen.