A method is disclosed for preparing cathodes loaded with manganese oxide
that are suitable for use in metal-air cells. The manganese oxide is
prepared from the reduction of potassium permanganate by sodium formate at
a substantially neutral pH level to produce manganese oxide sols. The sols
are then mixed with a carbon slurry to produce a colloidal suspension. The
suspension is subsequently waterproofed before being filtered, washed,
dried, and rolled to produce the active catalyst layer for the cathode
during discharge of the cell. The catalyst layer is then laminated with a
current collector and air diffusion layer. A separator is then added to
provide a carbon-based air cathode loaded with manganese oxide.
Un método se divulga para preparar los cátodos cargados con el óxido del manganeso que son convenientes para el uso en células del metal-aire. El óxido del manganeso es preparado de la reducción del permanganato del potasio por el formato de sodio en un nivel substancialmente neutral del pH para producir sols del óxido del manganeso. Los sols entonces se mezclan con una mezcla del carbón para producir una suspensión coloidal. La suspensión se impermeabiliza posteriormente antes de ser filtrada, el ser lavado, el ser secado, y el ser rodado para producir la capa activa del catalizador para el cátodo durante la descarga de la célula. La capa del catalizador entonces se lamina con una capa de la difusión del colector actual y del aire. Un separador entonces se agrega para proporcionar un cátodo carbo'n-basado del aire cargado con el óxido del manganeso.