Provided is a razor blade material which has excellent high hardness, high
strength and high corrosion resistance. The material is made of an Fe-base
alloy containing, by mass %, not less than 0.5% carbon, 9.0 to 14.0% Cr
and from more than zero to 8.0% Mo, wherein precipitates, which can be
observed at an optional cross section of the razor blade material, have a
diameter of less than 0.1 m. The alloy has preferably a chemical
composition of 0.5 to 5.0% carbon, 9.0 to 14.0% Cr and 0.5 to 8.0% Mo, 0.5
to 8.0% of B+Si, and the balance of Fe and unavoidable impurities.
Preferably, the alloy has a metal structure, not less than 30 volume % of
which is amorphous. The material has a thickness of 30 to 100 .mu.m. The
razor blade is preferably coated with polytetrafluoroethylene (PTFE).
Op voorwaarde dat een materiaal is van het scheermesblad dat uitstekende hoge hardheid, hoge sterkte en hoge corrosieweerstand heeft. Het materiaal wordt van Fe-Basis een legering gemaakt die, door massa %, niet minder dan 0,5% koolstof, 9,0 tot 14,0% Cr en van meer dan nul tot 8,0% Mo bevat, waarin de precipitaten, die bij een facultatieve dwarsdoorsnede van het materiaal van het scheermesblad kunnen worden waargenomen, een diameter van minder dan 0,1 m hebben. De legering heeft bij voorkeur een chemische samenstelling van 0,5 tot 5,0% koolstof, 9,0 tot 14,0% Cr en 0,5 tot 8,0% Mo, 0,5 tot 8,0% van B+Si, en het evenwicht van Fe en onvermijdelijke onzuiverheden. Bij voorkeur, heeft de legering een metaalstructuur, niet minder dan 30 volume% waarvan amorf is. Het materiaal heeft een dikte van mu.m. 30 tot 100 Het scheermesblad is bij voorkeur met een laag bedekt met polytetrafluoroethylene (PTFE).