A method of preparing graphite intercalation compounds in which graphite
particles are immersed in an aqueous electrolyte media comprising both an
acid and an oxidizing agent. The immersed graphite particles are subjected
to an anodic current and then removed from the electrolyte and rinsed with
a solvent. The excess solvent and electrolyte is then removed from the
graphite particles. The graphite particles may be placed in a plating
barrel which is immersed in the electrolyte and rotated while the graphite
particles are subjected to the current. The resultant intercalated
graphite has an expansion volume of from between about 100 ml/g to 2000
ml/g when heated to 1000.degree. C.
Un metodo di preparazione dei residui di intercalation della grafite in cui le particelle della grafite sono immerse nei mezzi acquosi dell'elettrolito che contengono sia un acido che un agente ossidante. Le particelle immerse della grafite sono sottoposte ad un corrente anodico ed allora sono rimosse dall'elettrolito e sono risciacquate con un solvente. Il solvente e l'elettrolito eccedenti allora è rimosso dalle particelle della grafite. Le particelle della grafite possono essere disposte in un barilotto di placcatura che è immerso nell'elettrolito ed è ruotato mentre le particelle della grafite sono sottoposte alla corrente. La grafite intercalata risultante ha un volume di espansione da in mezzo circa 100 ml/g - 2000 ml/g una volta riscaldata a 1000.degree. C.