Provided are a positive active material and a method of preparing for the
same. The positive active material comprises a core and a
surface-treatment layer on the core. The core includes at least one
lithiated compound, and the surface-treatment layer includes at least one
coating element-included oxide. The lithiated compound includes a
secondary particle of which average particle size is larger than or equal
to 1 .mu.m and less than 10 .mu.m. The secondary particle is formed of an
agglomeration of small primary particles of an average size of 1 to 3
.mu.m in diameter. The positive active material is prepared by coating the
lithiated compound with an organic solution or an aqueous solution
including a coating-element source and heat-treating the coated compound.
Vorausgesetzt ein positives aktives Material und eine Methode des Vorbereitens für dasselbe sind. Das positive aktive Material enthält einen Kern und eine Oberfläche-Behandlung Schicht auf dem Kern. Der Kern schließt ein mindestens lithiated Mittel mit ein, und die Oberfläche-Behandlung Schicht schließt mindestens ein beschichtendes Element-enthaltenes Oxid mit ein. Lithiated Mittel einschließt einen Sekundärpartikel, von dem durchschnittliche Teilchengröße größer als oder Gleichgestelltes zu 1 mu.m und weniger zu mu.m als 10 ist. Der Sekundärpartikel wird von einer Anhäufung der kleinen Primärpartikel einer durchschnittlichen Größe von mu.m 1 bis 3 im Durchmesser gebildet. Das positive aktive Material wird, indem man beschichtet, lithiated Mittel mit einer organischen Lösung oder einer wässerigen Lösung einschließlich eine Beschichtenelement Quelle und das Hitze-Behandeln des überzogenen Mittels vorbereitet.