A method for forming an implant having a desired shape includes the steps
of (a) forming a layer of ingredient powder having a predetermined
thickness composed of an ingredient powder, and (b) applying an reactant
liquid to the layer in accordance with the desired shape of the implant,
portions of the ingredient powder reacting with the reactant liquid being
hardened. The above steps are repeated to stack a plurality of the layers
having hardened portions, respectively, to form a three-dimensional
implant formed by a stack of the hardened portions of the layers of the
ingredient powder. The ingredient powder is a powder including at least
one of a-tricalcium phosphate and tetracalcium phosphate, and a Ca/P ratio
of the powder is within a range of 1.40 through 2.0.
Eine Methode für die Formung eines Implantats, das eine gewünschte Form hat, schließt die Schritte (a) einer Schicht Bestandteilpuders bildend ein, das eine vorbestimmte Stärke hat, die aus einem Bestandteilpuder besteht, und (b), eine Reaktionsmittelflüssigkeit an der Schicht in Übereinstimmung mit der gewünschten Form des Implantats anwendend, Teile des Bestandteilpuders, das mit der Reaktionsmittelflüssigkeit reagiert, die verhärtet wird. Die oben genannten Schritte werden wiederholt, um eine Mehrzahl der Schichten zu stapeln, die Teile beziehungsweise verhärtet werden um ein dreidimensionales Implantat zu bilden, das durch einen Stapel der verhärteten Teile der Schichten des Bestandteilpuders gebildet wird. Das Bestandteilpuder ist ein Puder einschließlich eins mindestens von ein-Trikalzium- Phosphat und von tetracalcium Phosphat, und ein Ca/P Verhältnis des Puders ist innerhalb eines Bereiches 1.40 bis 2.0.