Cellulosic materials such as wood chips, textile fibers and the like are
treated to produce products such as particle board having enhanced fire
and heat resistant properties. For example, wood chips are saturated with
an eqimolar aqueous solution of monoammonium phosphate and diammonium
phosphate. A metal hydroxide is added to the solution. The saturated wood
chips are dried and mixed with a modified glue composition. The glue that
which contains urea formaldehyde and/or phenolic resin is in powdered form
and dissolved in water. The treated wood chips and modified glue is then
mixed, formed into a mat and placed under pressure at about 120.degree. C.
for 8 to 15 minutes. The pressure may range from about 300 to 400 psi.
Os materiais cellulosic tais como as microplaquetas de madeira, as fibras de textile e o gosto são tratados para produzir produtos tais como a placa de partícula que realça o fogo e propriedades resistentes ao calor. Para o exemplo, as microplaquetas de madeira saturated com uma solução aqueous eqimolar do phosphate do monoammonium e do phosphate do diammonium. Um hydroxide do metal é adicionado à solução. As microplaquetas de madeira saturated são secadas e misturadas com uma composição modificada da colagem. A colagem isso que contem o formaldehyde do urea e/ou a resina phenolic está no formulário pulverizado e é dissolvida na água. As microplaquetas de madeira tratadas e a colagem modificada então são misturadas, dadas forma em uma esteira e colocadas sob a pressão aproximadamente em 120.degree. C. por 8 a 15 minutos. A pressão pode variar de aproximadamente 300 a 400 libras por polegada quadrada.