One aspect of the invention relates to a catalyst composite containing an
extruded catalyst support containing an extruded activated carbonaceous
material having specifically a defined pore structure. For example, the
extruded activated carbonaceous material may have pores wherein at least
about 40% of total Hg porosity occurs in pores having a diameter of about
200 .ANG. and larger. Alternatively the extruded activated carbonaceous
material may have a first set of pores having a pore diameter of at least
about 40 .ANG. and at most about 100 .ANG. with a porosity of at least
about 0.15 cc/g, and a second set of pores having a pore diameter of at
least about 5,000 .ANG. and at most about 20,000 .ANG. with a porosity of
at least about 0.3 cc/g.
Una funzione dell'invenzione riguarda un composto del catalizzatore che contiene un supporto sporto del catalizzatore che contiene un materiale carbonioso attivato sporto che ha specificamente una struttura definita del poro. Per esempio, il materiale carbonioso attivato sporto può avere pori in cui almeno circa 40% di porosità totale di Hg si presenta in pori che hanno un diametro di ANG. circa 200 e più grande. Alternativamente il materiale carbonioso attivato sporto può avere un primo insieme dei pori che hanno un diametro del poro almeno di ANG. circa 40 e tutt'al più ANG. Circa 100 con una porosità almeno di circa 0.15 cc/g e un secondo insieme dei pori che hanno un diametro del poro almeno di ANG. circa 5.000 e tutt'al più ANG. Circa 20.000 con una porosità almeno di circa 0.3 cc/g.