The lean NOx catalyst includes a substrate, an oxide support material,
preferably .gamma.-alumina deposited on the substrate and a metal or metal
oxide promoter or dopant introduced into the oxide support material. The
metal promoters or dopants are selected from the group consisting of
indium, gallium, tin, silver, germanium, gold, nickel, cobalt, copper,
iron, manganese, molybdenum, chromium cerium, and vanadium, and oxides
thereof, and any combinations thereof. The .gamma.-alumina preferably has
a pore volume of from about 0.5 to about 2.0 cc/g; a surface area of
between 80 and 350 m.sup.2 /g; an average pore size diameter of between
about 3 to 30 nm; and an impurity level of less than or equal to about 0.2
weight percent. In a preferred embodiment the .gamma.-alumina is prepared
by a sol-gel method, with the metal doping of the .gamma.-alumina
preferably accomplished using an incipient wetness impregnation technique.
Il catalizzatore di NOx della magra include un substrato, un materiale di sostegno dell'ossido, preferibilmente gamma.-allumina depositata sul substrato e un promotore dell'ossido di metallo o del metallo o dopant introdotto nel materiale di sostegno dell'ossido. I promotori o i dopant del metallo sono scelti dall'indio consistente del gruppo, gallio, latta, argento, germanio, oro, nichel, cobalto, rame, ferro, manganese, molibdeno, cerio del bicromato di potassio e vanadio ed ossidi di ciò e tutte le combinazioni di ciò. L'gamma.-allumina ha preferibilmente un volume del poro di circa 0.5 a circa 2.0 cc/g; un'area tra compreso 80 e 350 m.sup.2 /g; un diametro medio di formato del poro tra circa compreso 3 a 30 nm; e un livello di impurità di inferiore o uguale a i percento dei circa 0.2 pesi. In un metodo di realizzazione preferito l'gamma.-allumina è preparata con un metodo del solenoide-gel, con la verniciatura del metallo dell'gamma.-allumina compiuta preferibilmente usando una tecnica incipiente di impregnazione di umidità.