A high strength steel for dies has excellent machinability and including,
by weight, 0.005 to 0.1% C, not more than 1.5% Si, not more than 2.0% Mn,
from 3.0 to less than 8.0% Cr, not more than 4.0% Ni, 0.1 to 2.0% Al, not
more than 3.5% Cu, and balance of Fe and unavoidable impurities including
N and O, and which has a metal structure whose primary microstructure is
martensite, wherein N and O as impurities are restricted to amount ranges
of not more than 0.02% N and not more than 0.003% O. In the invention, an
improvement in the machinability in heavy cutting an improvement in the
precision electro discharge machining property and high-grade polishing
property can be achieved when the above high strength steel has a chemical
composition in which the value of (7.7.times.C (wt %))+(2.2.times.Si (wt
%))+271.2.times.S (wt %)) is preferably not less than 2.5 and more
preferably not more than 6.
Um aço elevado da força para dados tem o machinability excelente e incluir, pelo peso, 0.005 a 0.1% C, não mais de 1.5% o silicone, não mais manganês de 2.0%, de 3.0 menos de 8.0% ao cr, não mais Ni de 4.0%, o al 0.1 a 2.0%, não mais o cu de 3.5%, e o contrapeso do Fe e de impurezas unavoidable including N e O, e que tem uma estrutura do metal cujo o microstructure preliminar seja martensite, wherein N e O como impurezas são restringidos para atingir escalas de não mais de 0.02% N e de não mais de 0.003% O. Na invenção, uma melhoria no machinability no corte pesado uma melhoria na propriedade fazendo à máquina da descarga do eletro da precisão e na propriedade lustrando high-grade pode ser conseguida quando o aço elevado acima da força tem uma composição química em que o valor (7.7.times.C (peso %))+(2.2.times.Si (peso %))+271.2.times.S (peso %)) não é preferivelmente menos de 2.5 e mais preferivelmente não mais de 6.