Biaxially oriented, co-extruded polyester films comprising a base layer
consisting of at least 90 wt. % thermoplastic polyester, preferably
polyethylene terephthalate (PET), at least one sealable outer layer and a
second non-sealable outer layer and, optionally, other intermediate
layers, in addition to at least one flame-retardant agent, preferably
organic phosphorous compounds. The inventive films are characterized by
low inflammability, no embrittlement when subjected to thermal stress and
a surface which is devoid of troublesome opacity, and are suitable for a
multiplicity of uses both indoors and outside. The outer layers contain
anti-blocking agents such as silicic acid having a particle diameter of
preferably less than 50 nm and/or more than 2 .mu.m. Preferably, the
sealable outer layer consists of a copolyester which is made of ethylene
terephthalate and ethylene isophthalate units.
Biaxiaal georiënteerde, mede-uitgedreven polyesterfilms bestaand uit een basislaag die uit minstens 90 % gew. bestaat thermoplastische polyester, bij voorkeur polyethyleenterephthalate (HUISDIER), minstens één verzegelbare buitenlaag en een tweede niet verzegelbare buitenlaag en, naar keuze, andere middenlagen, naast minstens één flame-retardant agent, bij voorkeur organische fosforachtige samenstellingen. De vindingrijke films worden gekenmerkt door lage ontvlambaarheid, geen bros maken wanneer onderworpen aan thermische spanning en een oppervlakte die van lastige opaciteit verstoken is, en zijn buiten geschikt voor een multipliciteit van gebruik allebei binnen en. De buitenlagen bevatten anti-blocking agenten zoals siliciumzuur dat heeft een deeltjesdiameter van bij voorkeur dan minder 50 NM en/of mu.m. meer dan 2 Bij voorkeur, bestaat de verzegelbare buitenlaag uit een copolyester die gemaakt=wordt= van ethyleenterephthalate en ethyleen isophthalate eenheden.