A fine powder of metallic copper, suitable as a material for
electroconductive pastes, and having a BET diameter of 3 .mu.m or less,
large crystallite size, high dispersibility and particles of high
sphericity and a process for producing the same. More specifically, a fine
powder of metallic copper having a BET diameter of 3 .mu.m or less,
particles of high sphericity and crystallites of 0.1 to 10 .mu.m in size,
and more preferably containing oxygen at 0.3% by weight or less. Moreover,
the fine powder of metallic copper can be produced stably and efficiently
by blowing an ammonia-containing gas onto molten copper kept at
1120.degree. C. More specifically, it can be produced more stably and
efficiently by blowing ammonia at 0.015 L/minute or more per unit area
(cm.sup.2) of the molten copper.
Una polvere fine di rame metallico, adatte come materiale per le colle elettrocondutrici ed avere un diametro di SCOMMESSA di mu.m 3 o di di meno, grande formato della cristallite, alta disperdibilità e particelle di alta sfericità e di un procedimento per produrre lo stesso. Più specificamente, una polvere fine di rame metallico che ha un diametro di SCOMMESSA di mu.m 3 o di di meno, le particelle di alta sfericità e cristalliti di mu.m 0.1 - 10 nel formato e preferibilmente contenente ossigeno a 0.3% di peso o di meno. Inoltre, la polvere fine di rame metallico può essere prodotta stabile ed efficientemente saltando un gas ammonia-containing su rame fuso mantenuto a 1120.degree. C. Più specificamente, può essere prodotta più stabile ed efficientemente saltando l'ammoniaca a 0.015 L/minute o più per unità di superficie (cm.sup.2) del rame fuso.