Silicon nanocrystals with chemically accessible surfaces are produced in
solution in high yield. Silicon tetrahalide such as silicon tetrachloride
(SiCl.sub.4) can be reduced in organic solvents, such as
1,2-dimethoxyethane (glyme), with soluble reducing agents, such as sodium
naphthalenide, to give halide-terminated (e.g., chloride-terminated)
silicon nanocrystals, which can then be easily functionalized with alkyl
lithium, Grignard or other reagents to give easily processed silicon
nanocrystals with an air and moisture stable surface. The synthesis can be
used to prepare alkyl-terminated nanocrystals at ambient temperature and
pressure in high yield. The two-step process allows a wide range of
surface functionality.
Τα nanocrystals πυριτίου με τις χημικά προσιτές επιφάνειες παράγονται στη λύση στην υψηλή παραγωγή. Το tetrahalide πυριτίου όπως το τετραχλωρίδιο πυριτίου (SiCl.sub.4) μπορεί να μειωθεί στους οργανικούς διαλύτες, όπως 1,2-dimethoxyethane (glyme), με τους διαλυτούς μειώνοντας πράκτορες, όπως το naphthalenide νατρίου, για να δώσει τα αλογονίδιο-ολοκληρωμένα (π.χ., χλωρίδιο-ολοκληρωμένος) nanocrystals πυριτίου, τα οποία μπορούν έπειτα να είναι εύκολα με το αλκυλικό λίθιο, grignard ή άλλα αντιδραστήρια για να δώσουν τα εύκολα επεξεργασμένα nanocrystals πυριτίου με μια σταθερή επιφάνεια αέρα και υγρασίας. Η σύνθεση μπορεί να χρησιμοποιηθεί για να προετοιμάσει τα αλκυλικός-ολοκληρωμένα nanocrystals στην περιβαλλοντική θερμοκρασία και την πίεση στην υψηλή παραγωγή. Η σε δύο στάδια διαδικασία επιτρέπει ένα ευρύ φάσμα της λειτουργίας επιφάνειας.