The multilayer shrink film of the present invention provides very low
shrink tension approximating some PVC films, while providing relatively
high free shrink characteristics and relatively low shrink temperatures.
The preferred film has three layers including a relatively thick core
layer comprising a polymeric material or blend of polymeric materials
having a relatively low melting point, typically less than about
100.degree. C., two outer layers comprising a polymeric material or blend
of polymeric materials having a relatively high melting point, typically
greater than about 100.degree. C., the material of the outer layers having
a melting point at least about 10.degree. C. higher than the melting point
of the material of the core layer.
Разнослоистая пленка shrink присытствыющего вымысла обеспечивает очень низкое напряжение shrink приближаясь некоторые пленки pvc, пока обеспечивающ относительно высоко свободно характеристики shrink и относительно низкие температуры shrink. Предпочитаемая пленка имеет 3 слоя включая относительно толщиной слой сердечника состоя из полимерного материала или бленды полимерных материалов имея относительно низкую точку плавления, типично более менее чем о 100.degree. C, 2 наружных слоя состоя из полимерного материала или бленды полимерных материалов имея относительно высокую точку плавления, типично greater than о 100.degree. C, материал наружных слоев имея точку плавления по крайней мере о 10.degree. C более высоко чем точка плавления материала слоя сердечника.