An alkaline cell having an anode comprising zinc, an aqueous alkaline
electrolyte, a cathode mixture comprising cathode active material
comprising copper oxide or copper hydroxide. Graphitic carbon, preferably
expanded graphite or graphitic carbon nanofibers are added to the cathode
mixture thereby resulting in a sharp drop in cathode resistivity. The
cathode active material preferably comprises between about 80 and 92
percent by weight of the cathode. The sharp drop in cathode resistivity
resulting from the addition of expanded graphite or graphitic carbon
nanofibers makes the cell suitable for use as a primary alkaline cell
having good capacity. The graphitic carbon, preferably graphitic
nanofibers comprise preferably between about 4 and 10 percent by weight of
the cathode. The carbon nanofibers have an average diameter desirably less
than 500 nanometers, preferably between about 50 and 300 nanometers.
Une cellule alkaline ayant une anode comporter le zinc, un électrolyte alkalin aqueux, un mélange de cathode comportant le matériel actif de cathode comportant l'hydroxyde d'oxyde de cuivre ou de en cuivre. Le carbone graphitique, le graphite de préférence augmenté ou les nanofibers graphitiques de carbone sont ajoutés de ce fait au mélange de cathode ayant pour résultat une diminution sensible dans la résistivité de cathode. Le matériel actif de cathode comporte de préférence entre environ 80 et 92 pour cent du poids de la cathode. La diminution sensible dans la résistivité de cathode résultant de l'addition du graphite augmenté ou des nanofibers graphitiques de carbone rend la cellule appropriée pour l'usage comme cellule alkaline primaire ayant la bonne capacité. Le carbone graphitique, des nanofibers de préférence graphitiques comportent de préférence entre environ 4 et 10 pour cent du poids de la cathode. Les nanofibers de carbone ont un diamètre moyen de préférence moins de 500 nanomètres, de préférence entre environ 50 et 300 nanomètres.