A piezoelectric ceramic composition comprises a composite perovskite type
oxide of Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 and simple perovskite type
oxides of PbTiO.sub.3 and PbZrO.sub.3 as main components. The composition
range of the main components exists in an area surrounded by lines for
connecting respective composition points, i.e., a point A (X=40, Y=37,
Z=23), a point B (X=36, Y=37, Z=27), a point C (X=33, Y=40, Z=27), and a
point D (X=37, Y=40, Z=23) in a triangular coordinate system defined by
apexes of Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3, PbTiO.sub.3, and PbZrO.sub.3,
provided that Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 amounts to X molar %,
PbTiO.sub.3 amounts to Y molar %, and PbZrO.sub.3 amounts to Z molar %.
The composition makes it possible to realize a large strain amount while
suppressing the relative dielectric constant to be low. The composition is
preferably usable for an piezoelectric actuator of an ink-jet head.
Una composición de cerámica piezoeléctrica abarca un tipo compuesto óxido del perovskite de Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 y el tipo simple óxidos del perovskite de PbTiO.sub.3 y de PbZrO.sub.3 como componentes principales. La gama de la composición de los componentes principales existe en un área rodeada por las líneas para conectar puntos respectivos de la composición, es decir, un punto A (X=40, Y=37, Z=23), un punto B (X=36, Y=37, Z=27), un punto C (X=33, Y=40, Z=27), y un punto D (X=37, Y=40, Z=23) en un sistema coordinado triangular definido por los apexes de las cantidades Nb.sub.2/3)O.sub.3, PbTiO.sub.3, y PbZrO.sub.3, a condición de que las cantidades Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 asciende a X % molar, PbTiO.sub.3 de Pb(Ni.sub.1/3 a Y % molar, y PbZrO.sub.3 a la muela % de Z. la composición permite realizar una cantidad grande de la tensión mientras que suprimiendo la constante dieléctrica relativa para ser bajo. La composición es preferiblemente usable para un actuador piezoeléctrico de una cabeza de la inyección de tinta.