The present invention is directed to a process for making an absorbable
polylactone copolymer prepared in part from about 2 to about 80 mole
percent glycolide, which process utilizes a combination of a
monofunctional polymerization initiator and a di-functional polymerization
initiator, to achieve rates of crystallization of the copolymer of at
least about 2 times faster than the rate of crystallization of a copolymer
made by a similar process utilizing either the mono-functional or the
di-functional polymerization initiator alone. Absorbable polylactone
copolymers prepared by such processes and medical devices containing such
copolymers are also disclosed.
A invenção atual é dirigida a um processo para fazer um copolymer absorbable do polylactone preparado na parte de aproximadamente 2 a um glycolide de aproximadamente 80 por cento da toupeira, que o processo utilize uma combinação de um iniciador da polimerização do monofunctional e de um iniciador di-funcional da polimerização, para conseguir de mais rapidamente taxas da cristalização do copolymer ao menos aproximadamente 2 vezes do que a taxa da cristalização de um copolymer feito por um processo similar que utiliza o iniciador mono-funcional ou di-funcional da polimerização sozinho. Os copolymers absorbable do polylactone prepararam-se por tais processos e os dispositivos médicos que contêm tais copolymers são divulgados também.