Ultrafine powders of Li.sub.4 Ti.sub.5 O.sub.12 with particles in the size
range of 25-500 nm. The average size of particles is about 500 nm of less,
preferably about 300 nm or less. The particles are composed of
nanocrystallites, which have an average size about 30 nm. This invention
also includes the method of producing these ultrafine Li.sub.4 Ti.sub.5
O.sub.12 particles. The process utilizes (i) nanoparticles of TiO.sub.2,
(ii) a lithium salt, and (iii) an organic solvent with a boiling point in
the range of 70-230.degree. C. The process is carried out at pressures in
the range of 0.5 to 10 atmospheres. The inorganic salt of Li is mixed with
TiO.sub.2 nanoparticles (.about.20-25 nm) in the organic solvent. The
solution is heated to a temperature and at a pressure to facilitate the
diffusion of Li ions in to nanoparticles. After completion of the
reaction, the powder is heat treated in O.sub.2 or an inert gas to form
the desired phase.
Pós de Ultrafine de Li.sub.4 Ti.sub.5 O.sub.12 com partículas na escala do tamanho de 25-500 nm. O tamanho médio das partículas é aproximadamente 500 nm de menos, preferivelmente aproximadamente 300 nm ou menos. As partículas são compostas dos nanocrystallites, que têm um tamanho médio aproximadamente 30 nm. Esta invenção inclui também o método de produzir estas partículas do ultrafine Li.sub.4 Ti.sub.5 O.sub.12. O processo utiliza (i) nanoparticles de TiO.sub.2, (ii) um sal do lítio, e (iii) um solvente orgânico com um ponto fervendo na escala de 70-230.degree. C. O processo é realizado em pressões na escala de 0.5 a 10 atmosferas. O sal inorgánico do li é misturado com os nanoparticles TiO.sub.2 (about.20-25 nm) no solvente orgânico. A solução é aquecida a uma temperatura e em uma pressão facilitar dentro a difusão de íons do li aos nanoparticles. Após a conclusão da reação, o pó é calor tratado em O.sub.2 ou em um gás inerte para dar forma à fase desejada.