There is provided a process for producing a modified polymer rubber, which
comprises the steps of:
(1) reacting one part by mol of an organoalkali metal compound with
n.+-.0.7 (n is an integer of 3 or more) parts by mol of a specific
diphenyl compound to produce a reaction mixture,
(2) polymerizing in the presence of the produced reaction mixture an
aromatic vinyl monomer and a conjugated diene monomer in a hydrocarbon
solvent, and after completion of the polymerizing, stirring for at least
30 minutes, to produce a polymerization reaction mixture, and
(3) repeating such an operation n-2 times that (i) an aromatic vinyl
monomer and a conjugated diene monomer are added to the produced
polymerization reaction mixture, and polymerized, and (ii) after
completion of the polymerizing, stirring is carried out for at least 30
minutes, and thereby producing a modified polymer rubber, whose both ends
and n-2 positions in its chain are modified by the compound represented by
the formula (1).
Обеспечено процессу для производить доработанную резину полимера, которой состоит из шагов: (1) реагирующ одну часть mol смеси металла organoalkali с (н интежером 3 или больше) частями n.+-.0.7 mol специфически дифениловой смеси для того чтобы произвести смесь реакции, (2) полимеризующ in the presence of произведенная смесь реакции ароматичный мономер винила и проспряганный мономер диена в растворителе углерода, и после завершения полимеризовать, шевеля на по крайней мере 30 минут, для того чтобы произвести смесь реакции полимерности, и (3) повторяющ такие времена n-2 деятельности которые (i) ароматичному мономеру винила и проспряганному мономеру диена добавляют к произведенной смеси реакции полимерности, и полимеризовано, и (ii) после завершения полимеризовать, шевелить снесен вне для по крайней мере 30 минут, и таким образом производить доработанную резину полимера, которой и концы и положения n-2 в своей цепи доработаны смесью представленной формулой (1).