Steel strips and methods for producing steel strips are provided. In an
illustrated embodiment, a method includes continuously casting molten low
carbon steel into a strip of no more than 5 mm thickness having austenite
grains that are coarse grains of 100-300 micron width; and providing
desired yield strength in the cast strip by cooling the strip to transform
the austenite grains to ferrite in a temperature range between 850.degree.
C. and 400.degree. C. at a selected cooling rate of at least 0.01.degree.
C./sec to produce a microstructure that provides a strip having a yield
strength of at least 200 MPa. The low carbon steel produced desired
microstructure.
Las tiras y los métodos del acero para producir las tiras de acero se proporcionan. En una encarnación ilustrada, un método incluye continuo el acero de carbón bajo fundido de la colada en una tira de no más de 5 milímetros de grueso que tiene granos del austenite que sean granos gruesos de la anchura del micrón 100-300; y proporcionando fuerza deseada de la producción en la tira del molde refrescando la tira para transformar los granos del austenite a la ferrita en una gama de temperaturas entre 850.degree. C. y 400.degree. C. en un índice que se refresca seleccionado por lo menos de 0.01.degree. C./sec para producir una microestructura que proporciona una tira que tiene una fuerza de la producción de por lo menos 200 MPa. El acero de carbón bajo produjo microestructura deseada.