A foundation layer increasing adhesive properties to a substrate, another
foundation layer controlling orientation of an antiferromagnetic layer,
the antiferromagnetic layer including a disordered alloy of IrMn, a
pinning layer, and a cap protection layer are formed in the order on the
substrate. The pinning layer includes two layers having an exchange
coupling giving layer which exchange-couples to the antiferromagnetic
layer and an exchange coupling enhancement layer which enhances the
exchange coupling, the exchange coupling giving layer is made of a
ferromagnetic material including Co or a Co.sub.100-X Fe.sub.X alloy
(0.ltoreq.X<25) having face-centered cubic structure. The exchange
coupling enhancement layer is made of Fe or a Co.sub.100-Y Fe.sub.Y alloy
(25.ltoreq.Y.ltoreq.100) having body-centered cubic structure.
Ένα στρώμα ιδρύματος που αυξάνει τις συγκολλητικές ιδιότητες σε ένα υπόστρωμα, έναν άλλο ελέγχοντας προσανατολισμό στρώματος ιδρύματος ενός αντισιδηρομαγνητικού στρώματος, το αντισιδηρομαγνητικό στρώμα συμπεριλαμβανομένου ενός διαταραγμένου κράματος IrMn, ένα στρώμα ανάρτησης, και ένα στρώμα προστασίας ΚΑΠ διαμορφώνεται στη διαταγή σχετικά με το υπόστρωμα. Το στρώμα ανάρτησης περιλαμβάνει δύο στρώματα που έχουν μια σύζευξη ανταλλαγής που δίνει το στρώμα που τα ανταλλαγή-ζεύγη στο αντισιδηρομαγνητικό στρώμα και ένα στρώμα αυξήσεων συζεύξεων ανταλλαγής που ενισχύει τη σύζευξη ανταλλαγής, η σύζευξη ανταλλαγής που δίνει το στρώμα αποτελούνται από ένα σιδηρομαγνητικό υλικό συμπεριλαμβανομένου του κοβαλτίου ή ενός κράματος θο.σuψ.100-Χ Fe.sub.X (0.ltoreq.X