A method for preparing nylon 6 copolymer containing 5-sulfoisophthalate
salts comonomer. The method includes the steps of reacting
5-sulfoisophthalate salts ester with aliphatic diamine in a molar ratio of
2.about.20 at 160.about.200.degree. C., followed by completely removing
the unreacted aliphatic diamine, to obtain the intermediate compound with
terminal amine, 5-sulfobenzenediamide compound (formula III). Next,
caprolactam and aliphatic diacid (formula IV) are reacted at
200.about.260.degree. C. to form an oligomer with a low molecular weight.
5-Sulfobenzenediamide (formula III) and catalyst are then added into the
oligomer obtained in previous step to cause a polymerization reaction at
200.about.280.degree. C. to obtain nylon 6 copolymer containing
5-sulfoisophthalate salt comonomer. The molar ratio of E/C is
0.005.about.0.150 and the molar ratio of D/E is 1.05-1.00. Compounds
present in the water extract are greatly reduced.
Un metodo per la preparazione del copolimero del nylon 6 che contiene 5-sulfoisophthalate sala il comonomero. Il metodo include i punti di reazione dell'estere dei sali 5-sulfoisophthalate con la diammina alifatica in un rapporto molare di 2.about.20 a 160.about.200.degree. C., seguito completamente eliminando la diammina alifatica unreacted, per ottenere il residuo intermedio con l'ammina terminale, 5-sulfobenzenediamide residuo (formula Iii). Dopo, caprolattame e diacid alifatico (formula Iv) è reagita a 200.about.260.degree. C. per formare un oligomero con un peso a basso peso molecolare. 5-Sulfobenzenediamide (formula Iii) ed il catalizzatore allora sono aggiunti nell'oligomero ottenuto al punto precedente per causare una reazione di polimerizzazione a 200.about.280.degree. C. per ottenere il copolimero del nylon 6 che contiene il comonomero del sale 5-sulfoisophthalate. Il rapporto molare di E/C è 0.005.about.0.150 ed il rapporto molare di D/E è 1.05-1.00. I residui presenti nell'estratto dell'acqua notevolmente sono ridotti.