Steel sheet for porcelain enameling capable of realizing excellent enamel
adhesion with the steel sheet by direct-on enameling once is provided by
using a Ti-added steel sheet; there are also a method for producing the
same, as well as a porcelain enamel product and the method for producing
the same. A steel sheet for porcelain enameling is produced by providing a
Ni--Mo alloy plating film on a Ti-added steel sheet containing 0.01% by
weight (wherein, % represents "% by weight" hereinafter) or less of C,
0.5% or less of Mn, 0.04% or less of P, 0.04% or less of S, 0.01 to 0.50%
of Ti, and balance Fe accompanied by unavoidable impurities, and by then
performing heat treatment thereto to control the content of Ni, Mo, and Fe
present in the surface of the steel sheet in a predetermined range,
porcelain enamel is applied once and fired.
Stahlblech für das Porzellanemaillieren fähig zur Verwirklichung der ausgezeichneten Emailleadhäsion mit dem Stahlblech vorbei verweisen-auf einmal emaillieren wird vom Verwenden eines Ti-zusätzlichen Stahlblechs zur Verfügung gestellt; es gibt auch eine Methode für das Produzieren dasselbe, sowie ein Porzellanemailleprodukt und die Methode für das Produzieren dasselbe. Ein Stahlblech für das Porzellanemaillieren wird produziert, indem man ein Ni zur Verfügung stellt -- MO Legierung Überzugfilm auf einem Ti-zusätzlichen Stahlblech, das 0.01% nach Gewicht enthält (worin, % "% nach Gewicht" im folgenden darstellt) oder kleiner von C, 0.5% oder kleiner von Mangan, 0.04% oder kleiner von P, 0.04% oder kleiner von S, 0.01 bis 0.50% von Ti und Balance F.E., der von den unvermeidbaren Verunreinigungen begleitet wird und bis dahin dazu Wärmebehandlung, um durchführt den Inhalt von Ni, von MO und von F.E. zu steuern vorhanden ist in der Oberfläche des Stahlblechs in einer vorbestimmten Strecke, Porzellanemaille, wird einmal aufgetragen und abgefeuert, das.