Non-thermoplastic starch fibers having no melting point and having apparent
peak wet tensile stress greater than about 0.2 MegaPascals (MPa). The
fibers can be manufactured from a composition comprising a modified starch
and a cross-linking agent. The composition can have a shear viscosity from
about 1 Pascal.multidot.Seconds to about 80 Pascal.multidot.Seconds and an
apparent extensional viscosity in the range of from about 150
Pascal.multidot.Seconds to about 13,000 Pascal.multidot.Seconds. The
composition can comprise from about 50% to about 75% by weight of a
modified starch; from about 0.1% to about 10% by weight of an aldehyde
cross-linking agent; and from about 25% to about 50% by weight of water.
Prior to cross-linking, the modified starch can have a weight average
molecular weight greater than about 100,000 g/mol.
Nicht-thermoplastische Stärkefasern, die keinen Schmelzpunkt haben und offensichtlichen nassen dehnbaren Höchstdruck grösser als ungefähr 0.2 MegaPascals (MPa) haben. Die Fasern können von einem Aufbau hergestellt sein, der eine geänderte Stärke und ein Vernetzung Mittel enthält. Der Aufbau kann eine Scherviskosität von ungefähr 1 Pascal.multidot.Seconds zu ungefähr 80 Pascal.multidot.Seconds und eine offensichtliche extensional Viskosität in der Strecke von ungefähr 150 Pascal.multidot.Seconds haben zu ungefähr 13.000 Pascal.multidot.Seconds. Der Aufbau kann von ungefähr 50% bis ungefähr 75% nach Gewicht einer geänderten Stärke enthalten; von ungefähr 0.1% bis ungefähr 10% nach Gewicht eines Aldehydevernetzung Mittels; und von ungefähr 25% bis ungefähr 50% nach Gewicht Wasser. Vor Vernetzung kann die geänderte Stärke ein Gewichtdurchschnitt Molekulargewicht grösser als ungefähr 100.000 g/mol haben.