Aluminum-doped precipitated silicas having a BET surface area of more than
300 m.sup.2 /g and aluminum distributed uniformly in the silica particles
are prepared by sequentially heating a mixture of water and sodium
silicate at a temperature of from 70 to 86.degree. C. and adding sulfuric
acid until half of the sodium silicate is neutralized, then aging the
mixture for a time of from 30 to 120 minutes, adjusting the pH of the
mixture with sulfuric acid to a range of from 3.0 to 7.0, thereby
precipitating the aluminum-doped silica, filtering the aluminum-doped
silica from the mixture to form a filtercake and washing the filtercake,
followed by drying and/or grinding the washed filtercake. An aluminum salt
solution is metered into the mixture at step a) and/or step c). The
aluminum-doped precipitated silicas of the present invention may be used
in coatings for paper and other media intended for ink jet printing.
i siliconi precipitati Alluminio-verniciati che hanno un'area di SCOMMESSA di più di 300 m.sup.2 /g ed alluminio distribuiti uniformemente nelle particelle del silicone sono preparati in sequenza riscaldando una miscela del silicato del sodio e dell'acqua ad una temperatura di 70 a 86.degree. C. ed aggiungere acido solforico fino a neutralizzare la metà del silicato del sodio, allora invecchiante la miscela per un certo tempo di 30 - 120 minuti, registrante il pH della miscela con acido solforico ad una gamma di 3.0 - 7.0, quindi precipitante il silicone alluminio-verniciato, filtrante il silicone alluminio-verniciato dalla miscela per formare un filtercake e lavante il filtercake, seguito asciugando e/o macinando il filtercake lavato. Una soluzione salina di alluminio è misurata nella miscela al punto a) e/o al punto c). I siliconi precipitati alluminio-verniciati di presente invenzione possono essere usati in rivestimenti per carta ed in altri mezzi destinati alla stampa del getto di inchiostro.