Graphitized carbon powder are produced by carbonizing and expanding a pitch
by heating to form carbonaceous foam and by graphitizing before
pulverizing or graphitizing after pulverizing the carbonaceous foam. The
resultant graphitized carbon powders have an interplanar spacing (d002) of
graphite planes of less than 0.3370 nm. The powders preferably have an
average particle size of from 2 to 200 .mu.m. A thermally conductive
composition includes the graphitized carbon powders in a matrix. The
content of the powders is preferably 1 to 800 parts by weight relative to
100 parts by weight of the matrix. Thus, the graphitized carbon powders
that have excellent thermal conductivity and a thermally conductive
composition including such powders are provided.
La polvere grafitizzata del carbonio è prodotta carbonizzando ed espandendo un passo riscaldando per formare la gomma piuma carboniosa e grafitizzando prima della polverizzazione o della grafitizzazione dopo la polverizzazione della gomma piuma carboniosa. Le polveri grafitizzate risultanti del carbonio hanno un gioco interplanar (d002) dei piani della grafite di più meno di 0.3370 nm. Le polveri hanno preferibilmente una dimensione delle particelle media mu.m di 2 - 200. Una composizione termicamente conduttiva include le polveri grafitizzate del carbonio in una tabella. Il contenuto delle polveri è preferibilmente 1 - 800 parti di peso riguardante 100 parti a peso di la tabella. Quindi, le polveri grafitizzate del carbonio che hanno la conducibilità termica eccellente e una composizione termicamente conduttiva compreso tali polveri sono fornite.