An earth-acid metal is alloyed, whereby a metal foil comprising an
earth-acid metal as a main component, which surface can be roughened by
etching, can be obtained. An alloy of niobium with at least one element
selected from Groups 3 to 16 of the periodic table is preferred. This
alloy foil is etched, whereby an etched foil having an etching
magnification of about 50 times or more and containing pores having an
average pore size of about 0.05 to about 3 .mu.m to the depth
corresponding to at least about 5% or more of the foil thickness can be
obtained. A capacitor fabricated from this etched foil as at least one
part electrode and a dielectric material interposed between this one part
electrode and another part electrode, is also disclosed.
Металл земл-kisloty сплавлен, whereby фольгу металла состоя из металла земл-kisloty как главным образом компонент, который поверхность может быть сделана шероховатым путем вытравлять, можно получить. Предпочесн сплав ниобия при по крайней мере один элемент выбранный от групп 3 до 16 периодическаяа таблица. Эта фольга сплава вытравлена, whereby вытравленную фольгу имея увеличение вытравливания около 50 времен или больше и содержа поры имея средний размер поры около 0.05 к mu.m около 3 к глубине соответствуя к по крайней мере около 5% или больше из толщины фольги можно получить. Конденсатор изготовленный от этого вытравленная фольга как по крайней мере электрод одной части и диэлектрический материал interposed между этим электродом одной части и другим электродом части, также показан.