A hydrorefining catalyst of a hydrogenation active metal component
supported on a refractory porous carrier has a median pore diameter
determined by the nitrogen adsorption method of 8 to 20 nm, a pore volume
determined by the nitrogen adsorption method of 0.56 cm.sup.3 /g or
greater, and a pore volume of pores with a pore diameter of 50 nm or
larger determined by the mercury intrusion porosimetry method of 0.32
cm.sup.3 /g or greater. Both the demetallizing activity and metal
deposition capacity of the catalyst in hydrogenation and demetallizing of
heavy oil are high. The hydrorefining catalyst is obtained by kneading a
porous starting powder principally composed of .gamma.-alumina and having
a pore capacity of 0.75 m.sup.3 /g or larger and a mean pore diameter of
10 to 200 .mu.m, molding and calcining, and supporting an active metal
component on the product.
Un catalizador hydrorefining de un componente activo del metal de la hidrogenación apoyado en un portador poroso refractario tiene un diámetro mediano del poro determinado por el método de la adsorción del nitrógeno de 8 a 20 nm, un volumen del poro determinado por el método de la adsorción del nitrógeno de 0.56 cm.sup.3 /g o mayor, y un volumen del poro de poros con un diámetro del poro de 50 nm o un resuelto más grande por el método porosimetry de la intrusión del mercurio de 0.32 cm.sup.3 /g o mayor. La actividad demetallizing y la capacidad de la deposición del metal del catalizador en la hidrogenación y el demetallizing del aceite pesado son altos. El catalizador hydrorefining es obtenido amasando un polvo que comienza poroso integrado principalmente por el gamma.-alúmina y teniendo una capacidad del poro de 0.75 m.sup.3 /g o más grande y un diámetro malo del poro del mu.m 10 a 200, del moldeado y de la calcinación, y de apoyar un componente activo del metal en el producto.