A process for polymerizing vinyl chloride or a monomer mixture containing
vinyl chloride in an aqueous medium in a polymerization vessel fitted with
a reflux condenser, characterized by starting to add (A) an anti-foam
agent, and (B) a partially saponified polyvinyl alcohol with an average
degree of polymerization of 100 to 500 and a saponification degree of 75
to 85 mole %, to a reaction mixture during the operation of said reflux
condenser, and continuing the addition of (A) and (B) until recovery of
unreacted monomers from said polymerization vessel is completed, thereby
preventing the polymer slurry from foaming, rising, or scattering during
polymerization or recovery of unreacted monomers.
Un proceso para polimerizar el cloruro de vinilo o una mezcla del monomer que contiene el cloruro de vinilo en un medio acuoso en un recipiente de la polimerización cabido con un condensador de reflujo, caracterizado comenzando a agregar (a) un agente del antiespuma, y (b) un alcohol de polivinilo parcialmente saponificado con un grado medio de polimerización de 100 a 500 y un grado de la saponificación de 75 85 al topo %, a una mezcla de reacción durante la operación del condensador de reflujo dicho, y de continuar la adición de (a) y de (b) hasta la recuperación de monomers unreacted del recipiente dicho de la polimerización se termina, de tal modo evitando que la mezcla del polímero hacer espuma, el levantamiento, o disperse durante la polimerización o la recuperación de monomers unreacted.