An expandable vinyl chloride resin composition that the expansion ratio of
a vinyl chloride resin can be greatly increased by the use of thermally
decomposable inorganic blowing agents without the use of organic solvent
blowing agents, and which comprises 100 parts by weight of a vinyl
chloride resin, 5 to 30 parts by weight of, as a processing aid, a
(meth)acrylic acid ester polymer having a specific viscosity of not less
than 0.73 measured at 30.degree. C. with respect to a solution of 0.1 g of
the polymer dissolved in 100 ml of chloroform, and 2 to 25 parts by weight
of a thermally decomposable inorganic blowing agent.
Ein expandierbarer Vinylchlorverbindung Harzaufbau, daß das Expansion Verhältnis eines Vinylchlorverbindung Harzes durch den Gebrauch der thermisch zerlegbaren anorganischen Treibmittel ohne den Gebrauch der Treibmittel des organischen Lösungsmittels groß erhöht werden kann und das 100 Teile nach Gewicht eines Vinylchlorverbindung Harzes enthält, 5 bis 30 Teile nach Gewicht von, als verarbeitenhilfsmittel, a (das meth)acrylic saure Esterpolymer-Plastik, das eine spezifische Viskosität von nicht weniger als 0.73 gemessen an 30.degree hat. C. in Bezug auf eine Lösung von 0.1 g des Polymer-Plastiks löste sich in 100 ml Chloroform und 2 bis 25 Teilen nach Gewicht eines thermisch zerlegbaren anorganischen Treibmittels auf.